The materials of the race and ball of bearing require enough hardness and the following qualities:
(1). Large fatigue strength against repeated stress due to fatigue fracture of the race surface which governs the life of the bearings.
(2). High limit of elasticity and high yield strength to prevent deformation when a large load is applied per unit area.
(3). Large abrasion resistance against sliding friction between the retainer and the ball.
(4). High strength against crack due to impact load and failure caused by improper fitting etc.
(5).Small secular change in dimension and shape due to change of structure or internal stress.
Сталь GCr15 <JIS G4805> (Сталь з високовуглецевим хромом) порівняно добре відповідає вищенаведеному, а її хімічний склад показаний у наступній таблиці.
 

Хімічний склад високовуглецевої хромової сталі 

КласСтандартнийСимвол                                                   Хімічний склад (%)
ССіMnПSКр
1ГБGCr150,98-1,100,15-0,35<0,50<0,025<0,0251.30-1.60
DIN100Cr6
ASTME5200
JISSUJ2
2ГБ9Cr180,98-1,10<1.00<1.00<0,025<0,02516.00-18.00
DINX105CrMO17
ASTM440С
JISSUC440C

In order to maitain uniform qualit of materials, FK keeps fully equipped installations and performs strict acceotance tests and inspections based on the strict acceptance standards in addition to JIS-standards. 

Kinds of test done at the FK are mainly chemical analysis, magnetic exploration, ultrasonic exploration, corrosion by strong acid, inspection of structure by naked eyes, inspection of structure by microscope, crusher test and hardness etc.


2.Material of the Cage and the Rivet

 The material of cage is JIS G3141(Cold rolled carbon steel sheet and strip)SPCC, and it is formed by the press.
The material of the rivet is JIS G3507 (Low carbon steel wire rods)SWRCH 12A.
 

3.Materials of Housings

The material of the housings is FC200 JIS G5501 (Gray iron casting) and the mechanical properties are shown in the following table. 

                                      Mechanical properties of Gray cast iron HT200 

symbol

Thickness
(mm)

Dia. Of
testing bar
(mm)

Tension test

Traverse braking
Test

Pressure
Strength

Hardness
Test

Tensile
Strength

Bender
Strength

Deflection


Hardness

(kgf/mm2)

(kgf/mm)

(mm)

kgf/mm2

(HB)

HT200
(FC200)

Over 6-8

13

Over 23

53

1.8

75

187-255

Over 8-15

20

Over 22

45

2.5

75

170-241

Over 15-30

30

Over 20

40

2.5

75

170-241

Over 30-50

45

Over 17

34

3.0

75

170-241

Over 50

60

Over 16

31

4.5

75

163-229

Other Materials of Housings

Symbol

JIS number

FCD40(QT400)

JIS G5502

SPCC(08)

JIS G3141

SUS304

JIS G4304

4.Матеріали інших компонентів

Компоненти

Використовувані матеріали

Символи JIS

Номер JIS

Рукав для перехідника

Вуглецева сталь для машинобудування

S25C

JIS G4051

Гайка для перехідника

Вуглецева сталь для машинобудування

S25C

JIS G4051

Шайба для адаптера

Лист і смужка з холоднокатаного вуглецевої сталі

SPCC

JIS G3141

Сальник

Синтетичний нітриловий каучук

-

-

Слінгер

Лист і смужка з холоднокатаного вуглецевої сталі

SPCC

JIS G3141

Шестикутник встановлений гвинт

Сталь молібдену хрому нікелю

SCM 435

JIS G4105

Шестикутний ключ

Сталь молібдену хрому нікелю

SNCM630

JIS G4103

Змастіть сосок

Безкоштовна ріжуча латунна планка

C3604

JIS H3250